- 拉伸強度 [MPa]: 27.88
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 75 | 75 | |
| Tensile Strength, Yield | 27.88 MPa | 4044 psi | |
| Elongation at Yield | 483 % | 483 % | |
| 100% Modulus | 0.00399 GPa | 0.578 ksi | |
| 200% Modulus | 0.008887 GPa | 1.289 ksi | |
| 300% Modulus | 0.01461 GPa | 2.119 ksi | |
| Tear Strength | 59.7 kN/m | 341 pli | Die C |
| Taber Abrasion, mg/1000 Cycles | 0.090 | 0.090 | H-18, mg loss/rev |
| Compression Set | 56 % @Temperature 70.0 °C, Time 79200 sec | 56 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 20.0 min @Temperature 149 °C | 0.333 hour @Temperature 300 °F | |