- 拉伸強度 [MPa]: 21.48
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 90 | 90 | |
| Tensile Strength, Yield | 21.48 MPa | 3115 psi | |
| Elongation at Yield | 257 % | 257 % | |
| 100% Modulus | 0.01197 GPa | 1.736 ksi | |
| 200% Modulus | 0.02144 GPa | 3.109 ksi | |
| Tear Strength | 67.6 kN/m | 386 pli | Die C |
| Taber Abrasion, mg/1000 Cycles | 0.17 | 0.17 | H-18, mg loss/rev |
| Compression Set | 56 % @Temperature 70.0 °C, Time 79200 sec | 56 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 20.0 min @Temperature 149 °C | 0.333 hour @Temperature 300 °F | |