- 拉伸強度 [MPa]: 17.36
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 86 | 86 | |
| Tensile Strength, Yield | 17.36 MPa | 2518 psi | |
| Elongation at Yield | 222 % | 222 % | |
| 100% Modulus | 0.01225 GPa | 1.776 ksi | |
| 200% Modulus | 0.01740 GPa | 2.524 ksi | |
| Tear Strength | 53.7 kN/m | 306 pli | Die C |
| Taber Abrasion, mg/1000 Cycles | 0.21 | 0.21 | H-18, mg loss/rev |
| Compression Set | 60 % @Temperature 70.0 °C, Time 79200 sec | 60 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 20.0 min @Temperature 149 °C | 0.333 hour @Temperature 300 °F | |