- 拉伸強度 [MPa]: 23.8
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 80 | 80 | |
| Tensile Strength, Yield | 23.8 MPa | 3450 psi | |
| Elongation at Yield | 389 % | 389 % | |
| 100% Modulus | 0.007053 GPa | 1.023 ksi | |
| 200% Modulus | 0.01556 GPa | 2.257 ksi | |
| 300% Modulus | 0.02268 GPa | 3.289 ksi | |
| Tear Strength | 63.2 kN/m | 361 pli | Die C |
| Taber Abrasion, mg/1000 Cycles | 0.10 | 0.10 | H-18, mg loss/rev |
| Compression Set | 56 % @Temperature 70.0 °C, Time 79200 sec | 56 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 20.0 min @Temperature 149 °C | 0.333 hour @Temperature 300 °F | |