- 拉伸強度 [MPa]: 20.02
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 64 | 64 | |
| Tensile Strength, Yield | 20.02 MPa | 2903 psi | |
| Elongation at Yield | 398 % | 398 % | |
| 100% Modulus | 0.00382 GPa | 0.554 ksi | |
| 200% Modulus | 0.009611 GPa | 1.394 ksi | |
| 300% Modulus | 0.01509 GPa | 2.188 ksi | |
| Tear Strength | 47.4 kN/m | 270 pli | Die C |
| Taber Abrasion, mg/1000 Cycles | 0.090 | 0.090 | H-18, mg loss/rev |
| Compression Set | 63 % @Temperature 70.0 °C, Time 79200 sec | 63 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 20.0 min @Temperature 149 °C | 0.333 hour @Temperature 300 °F | |