- 拉伸強度 [MPa]: 11.9
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 71 | 71 | |
| Tensile Strength, Yield | 11.9 MPa | 1730 psi | |
| Elongation at Yield | 383 % | 383 % | |
| 100% Modulus | 0.00490 GPa | 0.710 ksi | |
| 200% Modulus | 0.01011 GPa | 1.467 ksi | |
| 300% Modulus | 0.01097 GPa | 1.591 ksi | |
| Tear Strength | 34.7 kN/m | 198 pli | Die C |
| Taber Abrasion, mg/1000 Cycles | 0.47 | 0.47 | H-18, mg loss/rev |
| Compression Set | 53 % @Temperature 70.0 °C, Time 79200 sec | 53 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 20.0 min @Temperature 149 °C | 0.333 hour @Temperature 300 °F | |