- 拉伸強度 [MPa]: 22.74
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 69 | 69 | |
| Tensile Strength, Yield | 22.74 MPa | 3298 psi | |
| Elongation at Yield | 401 % | 401 % | |
| 100% Modulus | 0.00485 GPa | 0.703 ksi | |
| 200% Modulus | 0.01188 GPa | 1.723 ksi | |
| 300% Modulus | 0.01780 GPa | 2.581 ksi | |
| Tear Strength | 52.3 kN/m | 298 pli | Die C |
| Taber Abrasion, mg/1000 Cycles | 0.060 | 0.060 | H-18, mg loss/rev |
| Compression Set | 61 % @Temperature 70.0 °C, Time 79200 sec | 61 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 20.0 min @Temperature 149 °C | 0.333 hour @Temperature 300 °F | |