- 拉伸強度 [MPa]: 18.22
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | 80 | 80 | |||
| Tensile Strength, Yield | 18.22 MPa | 2643 psi | |||
| Elongation at Yield | 423 % | 423 % | |||
| 100% Modulus | 0.00485 GPa | 0.704 ksi | |||
| 200% Modulus | 0.01042 GPa | 1.512 ksi | |||
| 300% Modulus | 0.01508 GPa | 2.187 ksi | |||
| Tear Strength | 35.0 kN/m | 200 pli | Die C | ||
| Compression Set | 58 % @Temperature 70.0 °C, Time 79200 sec | 58 % @Temperature 158 °F, Time 22.0 hour | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 12.0 min @Temperature 160 °C | 0.200 hour @Temperature 320 °F | Press cured | ||
| Descriptive Properties | |||||
| DIN Abrasion (mm3) | 120 | ||||