- 拉伸強度 [MPa]: 11.21
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 70 | 70 | |
| Tensile Strength, Yield | 11.21 MPa | 1626 psi | |
| Elongation at Yield | 523 % | 523 % | |
| 100% Modulus | 0.00177 GPa | 0.257 ksi | |
| 200% Modulus | 0.00405 GPa | 0.587 ksi | |
| 300% Modulus | 0.00681 GPa | 0.987 ksi | |
| Tear Strength | 33.3 kN/m | 190 pli | Die C |
| Compression Set | 39.7 % @Temperature 70.0 °C, Time 79200 sec | 39.7 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 4.90 min @Temperature 177 °C | 0.0817 hour @Temperature 350 °F | |