- 拉伸強(qiáng)度 [MPa]: 17.64
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | 85 | 85 | |||
| Tensile Strength, Yield | 17.64 MPa | 2558 psi | |||
| Elongation at Yield | 410 % | 410 % | |||
| 100% Modulus | 0.00509 GPa | 0.738 ksi | |||
| 200% Modulus | 0.01058 GPa | 1.534 ksi | |||
| 300% Modulus | 0.01501 GPa | 2.177 ksi | |||
| Tear Strength | 41.0 kN/m | 234 pli | Die C | ||
| Compression Set | 60 % @Temperature 70.0 °C, Time 79200 sec | 60 % @Temperature 158 °F, Time 22.0 hour | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 12.0 min @Temperature 160 °C | 0.200 hour @Temperature 320 °F | Press cured | ||
| Descriptive Properties | |||||
| DIN Abrasion (mm3) | 126 | ||||