- 拉伸強度 [MPa]: 18.73
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | 81 | 81 | |||
| Tensile Strength, Yield | 18.73 MPa | 2716 psi | |||
| Elongation at Yield | 461 % | 461 % | |||
| 100% Modulus | 0.00555 GPa | 0.805 ksi | |||
| 200% Modulus | 0.01122 GPa | 1.628 ksi | |||
| 300% Modulus | 0.01555 GPa | 2.256 ksi | |||
| Tear Strength | 46.0 kN/m | 262 pli | Die C | ||
| Compression Set | 57 % @Temperature 70.0 °C, Time 79200 sec | 57 % @Temperature 158 °F, Time 22.0 hour | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 10.0 min @Temperature 160 °C | 0.167 hour @Temperature 320 °F | Press cured | ||
| Descriptive Properties | |||||
| DIN Abrasion (mm3) | 120 | ||||