- 拉伸強度 [MPa]: 18.07
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | 83 | 83 | |||
| Tensile Strength, Yield | 18.07 MPa | 2621 psi | |||
| Elongation at Yield | 395 % | 395 % | |||
| 100% Modulus | 0.00574 GPa | 0.833 ksi | |||
| 200% Modulus | 0.01176 GPa | 1.706 ksi | |||
| 300% Modulus | 0.01610 GPa | 2.335 ksi | |||
| Tear Strength | 40.0 kN/m | 228 pli | Die C | ||
| Compression Set | 59 % @Temperature 70.0 °C, Time 79200 sec | 59 % @Temperature 158 °F, Time 22.0 hour | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 12.0 min @Temperature 160 °C | 0.200 hour @Temperature 320 °F | Press cured | ||
| Descriptive Properties | |||||
| DIN Abrasion (mm3) | 124 | ||||