- 拉伸強度 [MPa]: 15.89
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | 79 | 79 | |||
| Tensile Strength, Yield | 15.89 MPa | 2304 psi | |||
| Elongation at Yield | 717 % | 717 % | |||
| 100% Modulus | 0.00283 GPa | 0.410 ksi | |||
| 200% Modulus | 0.00541 GPa | 0.784 ksi | |||
| 300% Modulus | 0.008170 GPa | 1.185 ksi | |||
| Tear Strength | 64.0 kN/m | 365 pli | Die C | ||
| Compression Set | 79 % @Temperature 70.0 °C, Time 79200 sec | 79 % @Temperature 158 °F, Time 22.0 hour | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 6.00 min @Temperature 160 °C | 0.100 hour @Temperature 320 °F | Press cured | ||
| Descriptive Properties | |||||
| DIN Abrasion (mm3) | 140 | ||||