- 拉伸強(qiáng)度 [MPa]: 18.5
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | 82 | 82 | |||
| Tensile Strength, Yield | 18.50 MPa | 2683 psi | |||
| Elongation at Yield | 408 % | 408 % | |||
| 100% Modulus | 0.00550 GPa | 0.797 ksi | |||
| 200% Modulus | 0.0116 GPa | 1.68 ksi | |||
| 300% Modulus | 0.01618 GPa | 2.346 ksi | |||
| Tear Strength | 39.0 kN/m | 223 pli | Die C | ||
| Compression Set | 59 % @Temperature 70.0 °C, Time 79200 sec | 59 % @Temperature 158 °F, Time 22.0 hour | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 13.0 min @Temperature 160 °C | 0.217 hour @Temperature 320 °F | Press cured | ||
| Descriptive Properties | |||||
| DIN Abrasion (mm3) | 113 | ||||