- 拉伸強度 [MPa]: 18.88
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | 80 | 80 | |||
| Tensile Strength, Yield | 18.88 MPa | 2738 psi | |||
| Elongation at Yield | 524 % | 524 % | |||
| 100% Modulus | 0.00485 GPa | 0.703 ksi | |||
| 200% Modulus | 0.009701 GPa | 1.407 ksi | |||
| 300% Modulus | 0.01394 GPa | 2.022 ksi | |||
| Tear Strength | 60.0 kN/m | 342 pli | Die C | ||
| Compression Set | 69 % @Temperature 70.0 °C, Time 79200 sec | 69 % @Temperature 158 °F, Time 22.0 hour | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 11.0 min @Temperature 160 °C | 0.183 hour @Temperature 320 °F | Press cured | ||
| Descriptive Properties | |||||
| DIN Abrasion (mm3) | 136 | ||||