- 拉伸強度 [MPa]: 18.95
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | 80 | 80 | |||
| Tensile Strength, Yield | 18.95 MPa | 2749 psi | |||
| Elongation at Yield | 478 % | 478 % | |||
| 100% Modulus | 0.00527 GPa | 0.764 ksi | |||
| 200% Modulus | 0.01060 GPa | 1.538 ksi | |||
| 300% Modulus | 0.01483 GPa | 2.151 ksi | |||
| Tear Strength | 55.0 kN/m | 314 pli | Die C | ||
| Compression Set | 69 % @Temperature 70.0 °C, Time 79200 sec | 69 % @Temperature 158 °F, Time 22.0 hour | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 12.0 min @Temperature 160 °C | 0.200 hour @Temperature 320 °F | Press cured | ||
| Descriptive Properties | |||||
| DIN Abrasion (mm3) | 115 | ||||