- 拉伸強度 [MPa]: 17.89
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | 81 | 81 | |||
| Tensile Strength, Yield | 17.89 MPa | 2595 psi | |||
| Elongation at Yield | 410 % | 410 % | |||
| 100% Modulus | 0.00559 GPa | 0.811 ksi | |||
| 200% Modulus | 0.0114 GPa | 1.66 ksi | |||
| 300% Modulus | 0.01586 GPa | 2.301 ksi | |||
| Tear Strength | 38.0 kN/m | 217 pli | Die C | ||
| Compression Set | 60 % @Temperature 70.0 °C, Time 79200 sec | 60 % @Temperature 158 °F, Time 22.0 hour | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 8.00 min @Temperature 160 °C | 0.133 hour @Temperature 320 °F | Press cured | ||
| Descriptive Properties | |||||
| DIN Abrasion (mm3) | 123 | ||||