- 拉伸強度 [MPa]: 17.83
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | 79 | 79 | |||
| Tensile Strength, Yield | 17.83 MPa | 2586 psi | |||
| Elongation at Yield | 638 % | 638 % | |||
| 100% Modulus | 0.00367 GPa | 0.532 ksi | |||
| 200% Modulus | 0.007322 GPa | 1.062 ksi | |||
| 300% Modulus | 0.01091 GPa | 1.582 ksi | |||
| Tear Strength | 61.0 kN/m | 348 pli | Die C | ||
| Compression Set | 72 % @Temperature 70.0 °C, Time 79200 sec | 72 % @Temperature 158 °F, Time 22.0 hour | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 5.00 min @Temperature 160 °C | 0.0833 hour @Temperature 320 °F | Press cured | ||
| Descriptive Properties | |||||
| DIN Abrasion (mm3) | 136 | ||||