- 拉伸強度 [MPa]: 20.37
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 53 | 53 | |
| Tensile Strength, Yield | 20.37 MPa | 2955 psi | |
| Elongation at Yield | 530 % | 530 % | |
| 100% Modulus | 0.00103 GPa | 0.150 ksi | |
| 200% Modulus | 0.00299 GPa | 0.433 ksi | |
| 300% Modulus | 0.00724 GPa | 1.05 ksi | |
| Tear Strength | 25.6 kN/m | 146 pli | Die C |
| Taber Abrasion, mg/1000 Cycles | 0.10 | 0.10 | H-18, mg loss/rev |
| Compression Set | 55 % @Temperature 70.0 °C, Time 79200 sec | 55 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 20.0 min @Temperature 149 °C | 0.333 hour @Temperature 300 °F | |