- 拉伸強(qiáng)度 [MPa]: 16.83
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | 80 | 80 | |||
| Tensile Strength, Yield | 16.83 MPa | 2441 psi | |||
| Elongation at Yield | 437 % | 437 % | |||
| 100% Modulus | 0.00456 GPa | 0.662 ksi | |||
| 200% Modulus | 0.009460 GPa | 1.372 ksi | |||
| 300% Modulus | 0.0137 GPa | 1.98 ksi | |||
| Tear Strength | 44.0 kN/m | 251 pli | Die C | ||
| Compression Set | 76 % @Temperature 70.0 °C, Time 79200 sec | 76 % @Temperature 158 °F, Time 22.0 hour | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 15.0 min @Temperature 160 °C | 0.250 hour @Temperature 320 °F | Press cured | ||
| Descriptive Properties | |||||
| DIN Abrasion (mm3) | 139 | ||||