- 拉伸強度 [MPa]: 15.8
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | 80 | 80 | |||
| Tensile Strength, Yield | 15.8 MPa | 2290 psi | |||
| Elongation at Yield | 462 % | 462 % | |||
| 100% Modulus | 0.00400 GPa | 0.580 ksi | |||
| 200% Modulus | 0.008191 GPa | 1.188 ksi | |||
| 300% Modulus | 0.01205 GPa | 1.748 ksi | |||
| Tear Strength | 39.0 kN/m | 223 pli | Die C | ||
| Compression Set | 82 % @Temperature 70.0 °C, Time 79200 sec | 82 % @Temperature 158 °F, Time 22.0 hour | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 17.0 min @Temperature 160 °C | 0.283 hour @Temperature 320 °F | Press cured | ||
| Descriptive Properties | |||||
| DIN Abrasion (mm3) | 140 | ||||