- 拉伸強度 [MPa]: 20.98
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 57 | 57 | |
| Tensile Strength, Yield | 20.98 MPa | 3043 psi | |
| Elongation at Yield | 537 % | 537 % | |
| 100% Modulus | 0.00145 GPa | 0.210 ksi | |
| 200% Modulus | 0.00412 GPa | 0.598 ksi | |
| 300% Modulus | 0.008811 GPa | 1.278 ksi | |
| Tear Strength | 32.6 kN/m | 186 pli | Die C |
| Taber Abrasion, mg/1000 Cycles | 0.14 | 0.14 | H-18, mg loss/rev |
| Compression Set | 57 % @Temperature 70.0 °C, Time 79200 sec | 57 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 20.0 min @Temperature 149 °C | 0.333 hour @Temperature 300 °F | |