- 拉伸強度 [MPa]: 19.93
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 81 | 81 | |
| Tensile Strength, Yield | 19.93 MPa | 2891 psi | |
| Elongation at Yield | 345 % | 345 % | |
| 100% Modulus | 0.008708 GPa | 1.263 ksi | |
| 200% Modulus | 0.01675 GPa | 2.429 ksi | |
| 300% Modulus | 0.01753 GPa | 2.543 ksi | |
| Tear Strength | 58.1 kN/m | 332 pli | Die C |
| Taber Abrasion, mg/1000 Cycles | 0.11 | 0.11 | H-18, mg loss/rev |
| Compression Set | 61 % @Temperature 70.0 °C, Time 79200 sec | 61 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 20.0 min @Temperature 149 °C | 0.333 hour @Temperature 300 °F | |