- 拉伸強度 [MPa]: 20.76
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 77 | 77 | |
| Tensile Strength, Yield | 20.76 MPa | 3011 psi | |
| Elongation at Yield | 383 % | 383 % | |
| 100% Modulus | 0.00645 GPa | 0.935 ksi | |
| 200% Modulus | 0.01376 GPa | 1.996 ksi | |
| 300% Modulus | 0.01854 GPa | 2.689 ksi | |
| Tear Strength | 56.4 kN/m | 322 pli | Die C |
| Taber Abrasion, mg/1000 Cycles | 0.090 | 0.090 | H-18, mg loss/rev |
| Compression Set | 65 % @Temperature 70.0 °C, Time 79200 sec | 65 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 20.0 min @Temperature 149 °C | 0.333 hour @Temperature 300 °F | |