- 拉伸強度 [MPa]: 19.64
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 85 | 85 | |
| Tensile Strength, Yield | 19.64 MPa | 2849 psi | |
| Elongation at Yield | 281 % | 281 % | |
| 100% Modulus | 0.01260 GPa | 1.828 ksi | |
| 200% Modulus | 0.01873 GPa | 2.717 ksi | |
| Tear Strength | 60.4 kN/m | 345 pli | Die C |
| Taber Abrasion, mg/1000 Cycles | 0.17 | 0.17 | H-18, mg loss/rev |
| Compression Set | 59 % @Temperature 70.0 °C, Time 79200 sec | 59 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 20.0 min @Temperature 149 °C | 0.333 hour @Temperature 300 °F | |