- 拉伸強度 [MPa]: 18.64
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 77 | 77 | |
| Tensile Strength, Yield | 18.64 MPa | 2703 psi | |
| Elongation at Yield | 320 % | 320 % | |
| 100% Modulus | 0.007632 GPa | 1.107 ksi | |
| 200% Modulus | 0.01538 GPa | 2.231 ksi | |
| 300% Modulus | 0.0183 GPa | 2.65 ksi | |
| Tear Strength | 54.3 kN/m | 310 pli | Die C |
| Taber Abrasion, mg/1000 Cycles | 0.11 | 0.11 | H-18, mg loss/rev |
| Compression Set | 57 % @Temperature 70.0 °C, Time 79200 sec | 57 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 20.0 min @Temperature 149 °C | 0.333 hour @Temperature 300 °F | |