- 拉伸強(qiáng)度 [MPa]: 27.43
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 61 | 61 | |
| Tensile Strength, Yield | 27.43 MPa | 3978 psi | |
| Elongation at Yield | 464 % | 464 % | |
| 100% Modulus | 0.00285 GPa | 0.413 ksi | |
| 200% Modulus | 0.007212 GPa | 1.046 ksi | |
| 300% Modulus | 0.01320 GPa | 1.914 ksi | |
| Tear Strength | 45.3 kN/m | 258 pli | Die C |
| Taber Abrasion, mg/1000 Cycles | 0.070 | 0.070 | H-18, mg loss/rev |
| Compression Set | 61 % @Temperature 70.0 °C, Time 79200 sec | 61 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 20.0 min @Temperature 149 °C | 0.333 hour @Temperature 300 °F | |