- 拉伸強度 [MPa]: 20.07
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 70 | 70 | |
| Tensile Strength, Yield | 20.07 MPa | 2911 psi | |
| Elongation at Yield | 336 % | 336 % | |
| 100% Modulus | 0.01083 GPa | 1.571 ksi | |
| 200% Modulus | 0.01697 GPa | 2.461 ksi | |
| 300% Modulus | 0.01941 GPa | 2.815 ksi | |
| Tear Strength | 46.4 kN/m | 265 pli | Die C |
| Compression Set | 72 % @Temperature 70.0 °C, Time 79200 sec | 72 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 43.0 min @Temperature 154 °C | 0.717 hour @Temperature 310 °F | Press cured |