- 拉伸強度 [MPa]: 25.62
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 66 | 66 | |
| Tensile Strength, Yield | 25.62 MPa | 3716 psi | |
| Elongation at Yield | 519 % | 519 % | |
| 100% Modulus | 0.00476 GPa | 0.690 ksi | |
| 200% Modulus | 0.00687 GPa | 0.996 ksi | |
| 300% Modulus | 0.008563 GPa | 1.242 ksi | |
| Tear Strength | 37.1 kN/m | 212 pli | Die C |
| Compression Set | 62 % @Temperature 70.0 °C, Time 79200 sec | 62 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 19.0 min @Temperature 154 °C | 0.317 hour @Temperature 310 °F | Press cured |