- 拉伸強度 [MPa]: 21.9
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 89 | 89 | |
| Tensile Strength, Yield | 21.9 MPa | 3180 psi | |
| Elongation at Yield | 305 % | 305 % | |
| 100% Modulus | 0.01114 GPa | 1.616 ksi | |
| 200% Modulus | 0.02043 GPa | 2.963 ksi | |
| 300% Modulus | 0.02098 GPa | 3.043 ksi | |
| Tear Strength | 68.4 kN/m | 390 pli | Die C |
| Taber Abrasion, mg/1000 Cycles | 0.18 | 0.18 | H-18, mg loss/rev |
| Compression Set | 54 % @Temperature 70.0 °C, Time 79200 sec | 54 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 20.0 min @Temperature 149 °C | 0.333 hour @Temperature 300 °F | |