- 拉伸強度 [MPa]: 14.32
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 58 | 58 | |
| Tensile Strength, Yield | 14.32 MPa | 2077 psi | |
| Elongation at Yield | 463 % | 463 % | |
| 100% Modulus | 0.00228 GPa | 0.330 ksi | |
| 200% Modulus | 0.00394 GPa | 0.572 ksi | |
| 300% Modulus | 0.00505 GPa | 0.732 ksi | |
| Tear Strength | 29.1 kN/m | 166 pli | Die C |
| Compression Set | 52 % @Temperature 70.0 °C, Time 79200 sec | 52 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 22.0 min @Temperature 154 °C | 0.367 hour @Temperature 310 °F | Press cured |