- 拉伸強度 [MPa]: 29.19
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | >= 60 | >= 60 | |||
| Tensile Strength, Yield | 29.19 MPa | 4234 psi | |||
| Elongation at Yield | 594 % | 594 % | |||
| 100% Modulus | 0.00190 GPa | 0.276 ksi | |||
| 200% Modulus | 0.00410 GPa | 0.595 ksi | |||
| 300% Modulus | 0.007198 GPa | 1.044 ksi | |||
| Tear Strength | 39.8 kN/m | 227 pli | Die C | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 10.0 min @Temperature 68.3 °C | 0.167 hour @Temperature 155 °F | Press cured | ||
| Descriptive Properties | |||||
| DIN Abrasion (mm3) | 51.7 | ||||