- 拉伸強度 [MPa]: 30.19
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | >= 60 | >= 60 | |||
| Tensile Strength, Yield | 30.19 MPa | 4379 psi | |||
| Elongation at Yield | 653 % | 653 % | |||
| 100% Modulus | 0.00170 GPa | 0.247 ksi | |||
| 200% Modulus | 0.00270 GPa | 0.392 ksi | |||
| 300% Modulus | 0.00450 GPa | 0.653 ksi | |||
| Tear Strength | 36.2 kN/m | 207 pli | Die C | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 17.0 min @Temperature 68.3 °C | 0.283 hour @Temperature 155 °F | Press cured | ||
| Descriptive Properties | |||||
| DIN Abrasion (mm3) | 45 | ||||