- 拉伸強(qiáng)度 [MPa]: 20.99
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | >= 64 | >= 64 | |||
| Tensile Strength, Yield | 20.99 MPa | 3045 psi | |||
| Elongation at Yield | 606 % | 606 % | |||
| 100% Modulus | 0.00390 GPa | 0.566 ksi | |||
| 200% Modulus | 0.00550 GPa | 0.798 ksi | |||
| 300% Modulus | 0.00660 GPa | 0.957 ksi | |||
| Tear Strength | 33.3 kN/m | 190 pli | Die C | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 13.0 min @Temperature 68.3 °C | 0.217 hour @Temperature 155 °F | Press cured | ||
| Descriptive Properties | |||||
| DIN Abrasion (mm3) | 111.3 | ||||