- 拉伸強度 [MPa]: 31.5
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | >= 60 | >= 60 | |||
| Tensile Strength, Yield | 31.50 MPa | 4568 psi | |||
| Elongation at Yield | 603 % | 603 % | |||
| 100% Modulus | 0.00330 GPa | 0.479 ksi | |||
| 200% Modulus | 0.00480 GPa | 0.696 ksi | |||
| 300% Modulus | 0.00610 GPa | 0.885 ksi | |||
| Tear Strength | 35.0 kN/m | 200 pli | Die C | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 12.0 min @Temperature 68.3 °C | 0.200 hour @Temperature 155 °F | Press cured | ||
| Descriptive Properties | |||||
| DIN Abrasion (mm3) | 94.3 | ||||