- 拉伸強度 [MPa]: 27.1
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | >= 65 | >= 65 | |||
| Tensile Strength, Yield | 27.1 MPa | 3930 psi | |||
| Elongation at Yield | 584 % | 584 % | |||
| 100% Modulus | 0.00260 GPa | 0.377 ksi | |||
| 200% Modulus | 0.00590 GPa | 0.856 ksi | |||
| 300% Modulus | 0.009797 GPa | 1.421 ksi | |||
| Tear Strength | 39.2 kN/m | 224 pli | Die C | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 10.0 min @Temperature 68.3 °C | 0.167 hour @Temperature 155 °F | Press cured | ||
| Descriptive Properties | |||||
| DIN Abrasion (mm3) | 53 | ||||