- 拉伸強度 [MPa]: 30.1
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | >= 65 | >= 65 | |
| Tensile Strength, Yield | 30.10 MPa | 4365 psi | |
| Elongation at Yield | 558 % | 558 % | |
| 100% Modulus | 0.00250 GPa | 0.363 ksi | |
| 200% Modulus | 0.00570 GPa | 0.827 ksi | |
| 300% Modulus | 0.009797 GPa | 1.421 ksi | |
| Tear Strength | 36.2 kN/m | 207 pli | Die C |
| Compression Set | 32.2 % @Temperature 70.0 °C, Time 79200 sec | 32.2 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 10.0 min @Temperature 68.3 °C | 0.167 hour @Temperature 155 °F | |