- 拉伸強度 [MPa]: 26.79
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | >= 60 | >= 60 | |||
| Tensile Strength, Yield | 26.79 MPa | 3886 psi | |||
| Elongation at Yield | 620 % | 620 % | |||
| 100% Modulus | 0.00370 GPa | 0.537 ksi | |||
| 200% Modulus | 0.007901 GPa | 1.146 ksi | |||
| 300% Modulus | 0.01120 GPa | 1.624 ksi | |||
| Tear Strength | 36.8 kN/m | 210 pli | Die C | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 22.0 min @Temperature 68.3 °C | 0.367 hour @Temperature 155 °F | Press cured | ||
| Descriptive Properties | |||||
| DIN Abrasion (mm3) | 80.1 | ||||