- 拉伸強度 [MPa]: 28.5
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | >= 70 | >= 70 | |||
| Tensile Strength, Yield | 28.50 MPa | 4133 psi | |||
| Elongation at Yield | 544 % | 544 % | |||
| 100% Modulus | 0.00420 GPa | 0.609 ksi | |||
| 200% Modulus | 0.008998 GPa | 1.305 ksi | |||
| 300% Modulus | 0.01410 GPa | 2.045 ksi | |||
| Tear Strength | 38.3 kN/m | 219 pli | Die C | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 10.0 min @Temperature 68.3 °C | 0.167 hour @Temperature 155 °F | Press cured | ||
| Descriptive Properties | |||||
| DIN Abrasion (mm3) | 44.1 | ||||