- 拉伸強度 [MPa]: 24.9
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | >= 80 | >= 80 | |||
| Tensile Strength, Yield | 24.90 MPa | 3611 psi | |||
| Elongation at Yield | 442 % | 442 % | |||
| 100% Modulus | 0.007598 GPa | 1.102 ksi | |||
| 200% Modulus | 0.01530 GPa | 2.219 ksi | |||
| 300% Modulus | 0.02050 GPa | 2.973 ksi | |||
| Tear Strength | 36.0 kN/m | 205 pli | Die C | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 10.0 min @Temperature 68.3 °C | 0.167 hour @Temperature 155 °F | Press cured | ||
| Descriptive Properties | |||||
| DIN Abrasion (mm3) | 43.2 | ||||