- 拉伸強度 [MPa]: 23.39
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | >= 54 | >= 54 | |||
| Tensile Strength, Yield | 23.39 MPa | 3393 psi | |||
| Elongation at Yield | 597 % | 597 % | |||
| 100% Modulus | 0.00190 GPa | 0.276 ksi | |||
| 200% Modulus | 0.00290 GPa | 0.421 ksi | |||
| 300% Modulus | 0.00390 GPa | 0.566 ksi | |||
| Tear Strength | 36.8 kN/m | 210 pli | Die C | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 10.0 min @Temperature 68.3 °C | 0.167 hour @Temperature 155 °F | Press cured | ||
| Descriptive Properties | |||||
| DIN Abrasion (mm3) | 73.9 | ||||