- 拉伸強度 [MPa]: 27.79
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | >= 70 | >= 70 | |||
| Tensile Strength, Yield | 27.79 MPa | 4031 psi | |||
| Elongation at Yield | 554 % | 554 % | |||
| 100% Modulus | 0.00390 GPa | 0.566 ksi | |||
| 200% Modulus | 0.008501 GPa | 1.233 ksi | |||
| 300% Modulus | 0.01350 GPa | 1.958 ksi | |||
| Tear Strength | 39.3 kN/m | 224 pli | Die C | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 10.0 min @Temperature 68.3 °C | 0.167 hour @Temperature 155 °F | Press cured | ||
| Descriptive Properties | |||||
| DIN Abrasion (mm3) | 46.7 | ||||