- 拉伸強度 [MPa]: 19.2
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | >= 65 | >= 65 | |||
| Tensile Strength, Yield | 19.20 MPa | 2784 psi | |||
| Elongation at Yield | 576 % | 576 % | |||
| 100% Modulus | 0.00230 GPa | 0.334 ksi | |||
| 200% Modulus | 0.00500 GPa | 0.725 ksi | |||
| 300% Modulus | 0.008198 GPa | 1.189 ksi | |||
| Tear Strength | 31.2 kN/m | 178 pli | Die C | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 10.0 min @Temperature 68.3 °C | 0.167 hour @Temperature 155 °F | Press cured | ||
| Descriptive Properties | |||||
| DIN Abrasion (mm3) | 97.5 | ||||