- 拉伸強度 [MPa]: 32.0
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | >= 60 | >= 60 | |||
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | |||
| Elongation at Yield | 623 % | 623 % | |||
| 100% Modulus | 0.00140 GPa | 0.203 ksi | |||
| 200% Modulus | 0.00210 GPa | 0.305 ksi | |||
| 300% Modulus | 0.00330 GPa | 0.479 ksi | |||
| Tear Strength | 36.8 kN/m | 210 pli | Die C | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 10.0 min @Temperature 68.3 °C | 0.167 hour @Temperature 155 °F | Press cured | ||
| Descriptive Properties | |||||
| DIN Abrasion (mm3) | 30.8 | ||||