- 拉伸強度 [MPa]: 28.59
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | >= 68 | >= 68 | |||
| Tensile Strength, Yield | 28.59 MPa | 4147 psi | |||
| Elongation at Yield | 737 % | 737 % | |||
| 100% Modulus | 0.00180 GPa | 0.261 ksi | |||
| 200% Modulus | 0.00300 GPa | 0.435 ksi | |||
| 300% Modulus | 0.00490 GPa | 0.711 ksi | |||
| Tear Strength | 34.9 kN/m | 199 pli | Die C | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 17.0 min @Temperature 68.3 °C | 0.283 hour @Temperature 155 °F | Press cured | ||
| Descriptive Properties | |||||
| DIN Abrasion (mm3) | 51.8 | ||||