- 拉伸強度 [MPa]: 32.4
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | 67 | 67 | |||
| Tensile Strength, Yield | 32.4 MPa | 4700 psi | |||
| Elongation at Break | 570 % | 570 % | |||
| 300% Modulus | 0.0131 GPa | 1.90 ksi | |||
| Tear Strength | 65.6 kN/m | 374 pli | Die C; ASTM D624 | ||
| Abrasion | 355 | 355 | NBS Index | ||
| Compression Set | 22 % @Temperature 70.0 °C, Time 79200 sec | 22 % @Temperature 158 °F, Time 22.0 hour | Method B | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 60.0 min @Temperature 142 °C | 1.00 hour @Temperature 287 °F | |||
| Descriptive Properties | |||||
| Mooney Scorch | >30 | time to 10 point rise (minutes) at 250oF | |||
| 25 | time to 10 point rise (minutes) at 275oF | ||||