- 拉伸強(qiáng)度 [MPa]: 35.9
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | 75 | 75 | |||
| Tensile Strength, Yield | 35.9 MPa | 5200 psi | |||
| Elongation at Yield | 600 % | 600 % | |||
| 100% Modulus | 0.00224 GPa | 0.325 ksi | |||
| 300% Modulus | 0.00689 GPa | 1.00 ksi | |||
| Tear Strength | 52.6 kN/m | 300 pli | Graves | ||
| Compression Set | 70 % @Temperature 70.0 °C, Time 79200 sec | 70 % @Temperature 158 °F, Time 22.0 hour | Method B | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 15.0 min @Temperature 154 °C | 0.250 hour @Temperature 310 °F | |||
| Descriptive Properties | |||||
| 500% Modulus (ksi) | 2.85 | ||||
| Mooney Scorch | >= 55 | at 250oF; 22 minutes to a 10 point rise | |||