- 拉伸強度 [MPa]: 25.5
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | 68 | 68 | |||
| Tensile Strength, Yield | 25.5 MPa | 3700 psi | |||
| Elongation at Break | 550 % | 550 % | |||
| 300% Modulus | 0.00621 GPa | 0.900 ksi | |||
| Tear Strength | 64.7 kN/m | 369 pli | Die C; ASTM D624 | ||
| Abrasion | 365 | 365 | NBS Index | ||
| Compression Set | 24 % @Temperature 70.0 °C, Time 79200 sec | 24 % @Temperature 158 °F, Time 22.0 hour | Method B | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 60.0 min @Temperature 142 °C | 1.00 hour @Temperature 287 °F | |||
| Descriptive Properties | |||||
| Mooney Scorch | >30 | time to 10 point rise (minutes) at 250oF | |||
| 30 | time to 10 point rise (minutes) at 275oF | ||||