- 拉伸強度 [MPa]: 38.6
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | 64 | 64 | |||
| Tensile Strength, Yield | 38.6 MPa | 5600 psi | |||
| Elongation at Yield | 550 % | 550 % | |||
| 100% Modulus | 0.00276 GPa | 0.400 ksi | |||
| 300% Modulus | 0.0124 GPa | 1.80 ksi | |||
| Tear Strength | 43.8 kN/m | 250 pli | Graves | ||
| Abrasion | 350 | 350 | NBS Index | ||
| Compression Set | 35 % @Temperature 70.0 °C, Time 79200 sec | 35 % @Temperature 158 °F, Time 22.0 hour | Method B | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 15.0 min @Temperature 154 °C | 0.250 hour @Temperature 310 °F | |||
| Descriptive Properties | |||||
| 500% Modulus (ksi) | 5.6 | ||||
| Mooney Scorch | >= 32 | at 250oF; 23 minutes to a 10 point rise | |||