- 拉伸強度 [MPa]: 24.32
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 55 | 55 | |
| Tensile Strength, Yield | 24.32 MPa | 3528 psi | |
| Elongation at Yield | 695 % | 695 % | |
| 100% Modulus | 0.00131 GPa | 0.190 ksi | |
| 200% Modulus | 0.00173 GPa | 0.251 ksi | |
| 300% Modulus | 0.00253 GPa | 0.367 ksi | |
| Tear Strength | 29.4 kN/m | 168 pli | |
| Taber Abrasion, mg/1000 Cycles | 35 @Load 1.00 kg | 35 @Load 2.20 lb | H-18 wheel |
| Compression Set | 49.5 % @Temperature 70.0 °C, Time 79200 sec | 49.5 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 10.0 min @Temperature 155 °C | 0.167 hour @Temperature 311 °F | |